S-Plastics ValoxHX3061HPresin adalahPBT hanya untuk komposit/serat. Tidak dimaksudkan untuk cetakan injeksi. Biokompatibel. viskositas lebur: 250C pada 21,6 kgf adalah 1450-1850 poise.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 58 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 26 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3.7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 140 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2600 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 83 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2400 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 49 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 3.2 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 8.6 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2600 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 37 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 35 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 25 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 3 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 167 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 120 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 49 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 7.6E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.8E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 173 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 169 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 49 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.31 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 1.5 - 2 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 1.5 - 2 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/2,16 kgf | 50 | g/10 menit | ASTM D 1238 |
| Viskositas Peleburan | 100 | Pa-s | Metode S-Plastics |
| Kepadatan | 1.31 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.34 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 45 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:01/16/2007 | |||
| Parameter | ||
| Komposisi Ekstrusi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0 | % |
| Suhu Peleburan | 245 - 260 | °C |
| Barel - Zona 1 Suhu | 200 - 230 | °C |
| Barel - Zona 2 Suhu | 240 - 255 | °C |
| Barel - Zona 3 Suhu | 240 - 275 | °C |
| Barel - Zona 4 Suhu | 240 - 275 | °C |
| Suhu adaptor | 240 - 275 | °C |
| Suhu mati | 240 - 275 | °C |
| Suhu Mandi Air | 25 - 35 | °C |
| Sumber GMD, terakhir diperbarui:01/16/2007 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |