S-Plastics ValoxFXV310SKresinadalah resin injeksi PBT yang tidak diperkuat Visualfx* dengan karakteristik aliran yang tinggi dan mengandung berkilau logam.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 17 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 20 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 100 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2700 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 89 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2410 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 9 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 58 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 7 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 15 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2750 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2750 | MPa | ISO 178 |
| Kekerasan, H358/30 | 85 | MPa | ISO 2039-1 |
| Kekerasan, Rockwell R | 117 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 42 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 58 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 56 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m2 | ISO 179/1eA |
| Charpy Impact, bertanduk, 23°C | 3 | kJ/m2 | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 185 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 55 | °C | ASTM D 648 |
| CTE, -20°C sampai 150°C, xflow | 1.3E-04 | 1/°C | ASTM E 831 |
| CTE, 0°C sampai 100°C, aliran | 1.3E-04 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.16 | W/m-°C | ISO 8302 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 185 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 187 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 160 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 55 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.31 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 1.9 - 2.4 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/2,16 kgf | 27.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.31 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.34 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 18 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3.3 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 3.1 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.002 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.02 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 600 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94HB (3) ((4) | 1.47 | mm | UL 94 oleh GE |
| UL Compliant, 94HB Flame Class Rating 2nd value (3) ((4) | 3.12 | mm | UL 94 oleh GE |
| Indeks Oksigen (LOI) | 20 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:11/02/2006 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 270 | °C |
| Suhu Nozzle | 240 - 260 | °C |
| Suhu depan - Zona 3 | 245 - 265 | °C |
| Tengah - Zona 2 Suhu | 240 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Suhu Cetakan | 40 - 100 | °C |
| Sumber GMD, terakhir diperbarui:11/02/2006 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox FXV310SK.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|