SabikCycoloy C6600resin adalahNon-brominated, non-chlorinated FR PC+ABS dengan aliran seimbang, dampak dan stabilitas hidrolisis untuk berbagai aplikasi termasuk peralatan bisnis, monitor, kandang, antara lain.
| Properti Tipikal (1) | Aliran/Dampak yang Lebih Baik Saldo |
CX7110 | Tambahan Informasi |
| Mekanis Tekanan tarik, yld, tipe I, 50 mm/menit |
ValueImprovedUnit UL 63 KinerjaMPa |
CX7240ASTMSstandardInfo tambahan D 638 | |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 49 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 80 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 3000 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 94 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2620 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 550 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 51 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, -30°C | 51 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 99 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 83 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 98 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 90 | °C | ASTM D 648 |
| Indeks suhu relatif, Elec | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 70 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 80 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.19 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.11 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/2,16 kgf | 21.5 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 17 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 2.7 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.7 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.004 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.006 | - | IEC 60250 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-2 Flame Class Rating (3) | 0.75 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL diakui, 94-5VB rating (3) | 2 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:07/25/2005 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 245 - 275 | °C |
| Suhu Nozzle | 245 - 275 | °C |
| Suhu depan - Zona 3 | 245 - 275 | °C |
| Tengah - Zona 2 Suhu | 220 - 275 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 255 | °C |
| Suhu Cetakan | 60 - 80 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 30 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:07/25/2005 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy C6600.pdf |
|