S-Plastics Valox412Eresin adalah 20% GR, peningkatan kinerja mekanik vs PBT tidak diperkuat. non-retardant api. untuk lampu sorot, rumah peralatan dan pegangan.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 99 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 155 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 5170 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 119 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 694 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 69 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 211 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 201 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 3.42E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C sampai 138°C, aliran | 3.42E-05 | 1/°C | ASTM E 831 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.45 | - | ASTM D 792 |
| Volume Spesifik | 0.68 | cm3/g | ASTM D 792 |
| Penyerapan air, 24 jam | 0.06 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 1,5-3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2-4,6 mm | 0.6 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 1,5-3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2-4,6 mm | 0.8 - 1.1 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.7E+16 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 18.3 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 22.4 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 100 Hz | 3.5 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3.5 | - | ASTM D 150 |
| Faktor Dissipasi, 100 Hz | 0.001 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.02 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:12/29/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 265 | °C |
| Suhu Nozzle | 245 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 265 | °C |
| Tengah - Zona 2 Suhu | 245 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 255 | °C |
| Suhu Cetakan | 65 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.025 - 0.038 | mm |
| Sumber GMD, terakhir diperbarui:12/29/1999 | ||
|