SabikCycoloy C4210resin adalah10% GR PC + ABS. ketahanan panas tinggi. kekuatan / kekakuan yang sangat baik. dampak / penampilan yang baik. panel instrumen otomotif.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 75 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 75 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 3 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 4410 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 120 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3720 | MPa | ASTM D 790 |
| Tekanan tarik, pecah, 5 mm/menit | 70 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 3.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 4000 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 120 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3800 | MPa | ISO 178 |
| Kekerasan, H358/30 | 116 | MPa | ISO 2039-1 |
| Kekerasan, Rockwell R | 121 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 507 | J/m | ASTM D 4812 |
| Izod Impact, tidak diukir, -30°C | 587 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 122 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 90 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 20 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, -30°C | 16 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 35 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 11 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 9 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 11 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 35 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 134 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 125 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 127 | °C | ASTM D 648 |
| Konduktivitas Termal | 0.2 | W/m-°C | ISO 8302 |
| Vicat Softening Temperature, Tingkat B/50 | 134 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 136 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 134 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 120 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.22 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.3 - 0.5 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.3 - 0.5 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 22 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.22 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 15 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Sumber GMD, terakhir diperbarui:11/29/2002 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 100 - 105 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 260 - 290 | °C |
| Suhu Nozzle | 260 - 290 | °C |
| Suhu depan - Zona 3 | 255 - 290 | °C |
| Tengah - Zona 2 Suhu | 255 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 280 | °C |
| Suhu Cetakan | 75 - 100 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 30 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:11/29/2002 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy C4210.pdf |
|