S-Plastics ValoxEXVX1364resin adalah16% GF PBT, tahan api Non-Brominated & Non-Chlorinated
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 80 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 80 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 7500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 125 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 6200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/120 | 200 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.3 - 0.8 | % | Metode S-Plastics |
| Kepadatan | 1.5 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 15 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:10/30/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 245 - 260 | °C |
| Suhu Nozzle | 230 - 255 | °C |
| Suhu depan - Zona 3 | 240 - 260 | °C |
| Tengah - Zona 2 Suhu | 235 - 250 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 240 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Suhu Cetakan | 40 - 100 | °C |
| Sumber GMD, terakhir diperbarui:10/30/2008 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox EXVX1364.pdf |
|