SabikCycoloy C3600resin adalahkelas FR PC+ABS yang dikembangkan untuk proses ekstrusi.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Taber Abrasion, CS-17, 1 kg | 54 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 5 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 65 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 45 | % | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 35 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2700 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 100 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2800 | MPa | ISO 178 |
| Kekerasan, H358/30 | 118 | MPa | ISO 2039-1 |
| Kekerasan, Rockwell R | 124 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*3 +23°C | 45 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*3 -30°C | 14 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 45 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 14 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Konduktivitas Termal | 0.2 | W/m-°C | ISO 8302 |
| CTE, -40°C sampai 40°C, aliran | 7.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Uji tekanan bola, perkiraan maksimum | 100 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 111 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 113 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 104 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 92 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 60 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.4 - 0.6 | % | Metode S-Plastics |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.6 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 9 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan Dielektrik, dalam minyak, 0,8 mm | 35 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 25 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 17 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 2.8 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.7 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.004 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.006 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 600 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL diakui, 94-5VB rating (3) | 2.5 | mm | UL 94 |
| Glow Wire Flammability Index 850°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Glow Wire Flammability Index 960°C, melewati pada | 3.2 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 32 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:06/05/1998 | |||
| Parameter | ||
| Ekstrusi Profil | Nilai | Satuan |
| Suhu Pengeringan | 80 - 85 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Suhu Peleburan | 230 - 270 | °C |
| Barel - Zona 1 Suhu | 235 - 260 | °C |
| Barel - Zona 2 Suhu | 240 - 265 | °C |
| Barel - Zona 3 Suhu | 245 - 270 | °C |
| Barel - Zona 4 Suhu | 245 - 270 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu adaptor | 245 - 270 | °C |
| Suhu mati | 235 - 260 | °C |
| Suhu Kalibrator | 60 - 80 | °C |
| Sumber GMD, terakhir diperbarui:06/05/1998 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics cycoloy C3600.pdf |
|