SabikCycoloy C1200HFMresin adalahVersi PC + ABS-MAGIX dalam berbagai warna logam. karakteristik panas tinggi / aliran yang baik. peralatan, otomotif / telekomunikasi.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 51 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 44 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 50 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2480 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 75 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2410 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 15 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2400 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 82 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2400 | MPa | ISO 178 |
| Kekerasan, H358/30 | 121 | MPa | ISO 2039-1 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 427 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 40 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 24 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 12 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 25 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 13 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 143 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 131 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 112 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.2E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 80°C, aliran | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 128 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 130 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 128 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 108 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 105 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 105 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.18 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 22 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 22 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi busur, Tungsten {PLC} | 3 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Sumber GMD, terakhir diperbarui:04/11/2001 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 105 - 110 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 275 - 300 | °C |
| Suhu Nozzle | 275 - 300 | °C |
| Suhu depan - Zona 3 | 260 - 300 | °C |
| Tengah - Zona 2 Suhu | 255 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 290 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 30 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:04/11/2001 | ||