S-Plastics Valox357TFresin adalah Unreinforced, dampak dimodifikasi, UL94 V-0 dinilai, tidak ada PTFE.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 48 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 48 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 110 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2200 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 82 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 82 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2060 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 534 | J/m | ASTM D 256 |
| Gardner, 23°C | 43 | J | ASTM D 3029 |
| Gardner yang dimodifikasi, 23°C | 43 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 145 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 99 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 137 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 98 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.18E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C sampai 138°C, aliran | 1.24E-04 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 120 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 120 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 140 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.34 | - | ASTM D 792 |
| Volume Spesifik | 0.75 | cm3/g | ASTM D 792 |
| Penyerapan air, 24 jam | 0.08 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 0,75-2,3 mm | 0.8 - 1.1 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 2,3-4,6 mm | Satu, satu.4 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 0,75-2,3 mm | 0.9 - 1.3 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 2,3-4,6 mm | 1.2 - 1.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 8 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.2E+16 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 18.5 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 25.1 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 18.5 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 100 Hz | 3.2 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3.2 | - | ASTM D 150 |
| Faktor Dissipasi, 100 Hz | 0.003 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.03 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 4 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 3 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 2 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:04/28/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 265 | °C |
| Suhu Nozzle | 245 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 265 | °C |
| Tengah - Zona 2 Suhu | 245 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 255 | °C |
| Suhu Cetakan | 50 - 75 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.025 - 0.038 | mm |
| Sumber GMD, terakhir diperbarui:04/28/2004 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox 357TF.pdf |
|