S-Plastics Valox350Uresin adalah dampak dimodifikasi, UV stabil, tahan api poliester dengan rating internal glowwire 850C pada 1,6mm lempeng plak.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 56 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 50 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 100 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2250 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 88 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2250 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 758 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 130 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 82 | °C | ASTM D 648 |
| CTE, -40°C sampai 60°C, aliran | 1.98E-04 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 80 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 80 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.3 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.14 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | Satu, satu.4 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 16 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+15 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+15 | Ohm | ASTM D 257 |
| Permittivitas relatif, 50/60 Hz | 0 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 0.01 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 2.8 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 2.7 | - | ASTM D 150 |
| Indeks Pelacakan Perbandingan | 225 | V | IEC 60112 |
| Sumber GMD, terakhir diperbarui:06/18/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Suhu Peleburan | 235 - 265 | °C |
| Suhu Cetakan | 40 - 60 | °C |
| Sumber GMD, terakhir diperbarui:06/18/1999 |
|