S-Plastics ValoxEXVX1258resinadalah lingkungan yang bertanggung jawab tahan api, 30% serat kaca diperkuat PBT resin injeksi cetakan.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 106 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 106 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 1.7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.7 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 11000 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 177 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 8950 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 97 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 97 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 10700 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 180 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 9100 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 89 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 75 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 9 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 7 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 21 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 156 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 191 | °C | ASTM D 648 |
| CTE, -40°C sampai 150°C, aliran | 2.03E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 150°C, xflow | 1.02E-04 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 2.03E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 1.02E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 156 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 156 | °C | ISO 306 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.64 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 26 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.64 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.07 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 18 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:04/26/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 270 | °C |
| Suhu Nozzle | 240 - 260 | °C |
| Suhu depan - Zona 3 | 245 - 265 | °C |
| Tengah - Zona 2 Suhu | 240 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Suhu Cetakan | 40 - 100 | °C |
| Sumber GMD, terakhir diperbarui:04/26/2007 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox EXVX1258.pdf |
|