S-Plastics Valox315Gresin adalah Unreinforced, ekstrusi. tidak dimaksudkan untuk Injection Molding. viskositas tinggi. halus menggiling. viskositas leleh antara 7500 dan 9500 poise.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 51 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 300 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 82 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2340 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 117 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1602 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Gardner yang dimodifikasi, 23°C | 40 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 154 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 54 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.1E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C sampai 138°C, aliran | 1.39E-04 | 1/°C | ASTM E 831 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.31 | - | ASTM D 792 |
| Volume Spesifik | 0.76 | cm3/g | ASTM D 792 |
| Penyerapan air, 24 jam | 0.08 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 0,75-2,3 mm | 0.9 - 1.6 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 2,3-4,6 mm | 1.5 - 2.3 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 0,75-2,3 mm | Satu, satu.7 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 2,3-4,6 mm | 1.6 - 2.4 | % | Metode S-Plastics |
| Viskositas Peleburan | 700 | Pa-s | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >4.E+16 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 15.7 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 23.2 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 100 Hz | 3.3 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3.1 | - | ASTM D 150 |
| Faktor Dissipasi, 100 Hz | 0.002 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.02 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:01/05/2000 | |||
| Parameter | ||
| Komposisi Ekstrusi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0 | % |
| Suhu Peleburan | 245 - 260 | °C |
| Barel - Zona 1 Suhu | 200 - 230 | °C |
| Barel - Zona 2 Suhu | 240 - 255 | °C |
| Barel - Zona 3 Suhu | 240 - 275 | °C |
| Barel - Zona 4 Suhu | 240 - 275 | °C |
| Suhu adaptor | 240 - 275 | °C |
| Suhu mati | 240 - 275 | °C |
| Suhu Mandi Air | 25 - 35 | °C |
| Sumber GMD, terakhir diperbarui:01/05/2000 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox 315G.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|