S-Plastics Valox310SE0resin adalah resin injeksi PBT tahan api yang tidak diperkuat.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 58 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 58 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 20 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 20 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2820 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 101 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2620 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 19 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 20 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2800 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2600 | MPa | ISO 178 |
| Kekerasan, H358/30 | 105 | MPa | ISO 2039-1 |
| Kekerasan, Rockwell R | 120 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1602 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 37 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 22 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 200 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 3 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m2 | ISO 179/1eA |
| Charpy Impact, bertanduk, 23°C | 4 | kJ/m2 | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 165 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 74 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 162 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 71 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.92E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.92E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C sampai 138°C, aliran | 1.31E-04 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.24 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 60°C, aliran | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat A/50 | 212 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 165 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 165 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 135 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 60 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 120 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 120 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 140 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.4 | - | ASTM D 792 |
| Volume Spesifik | 0.71 | cm3/g | ASTM D 792 |
| Penyusutan jamur pada batang tarik, aliran (2) | 1.1 - 1.8 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 1.5 - 2.3 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 0,75-2,3 mm | 0.9 - 1.6 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 2,3-4,6 mm | 1.5 - 2.3 | % | Metode S-Plastics |
| Penyusutan jamur pada batang tarik, xflow (2) | 0.9 - 1.9 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 0,75-2,3 mm | Satu, satu.7 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 2,3-4,6 mm | 1.6 - 2.4 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/2,16 kgf | 8.6 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.4 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.36 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 8 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Kekuatan dielektrik, di udara, 3,2 mm | 18.4 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 22 | kV/mm | ASTM D 149 |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 4 | Kode PLC | UL 746A |
| Resistensi busur tegangan tinggi {PLC) | 6 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 3 | Kode PLC | UL 746A |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan dielektrik, waktu pendek, 1,0 mm | 18 | kV/mm | IEC 60243-1 |
| Kekuatan Dielektrik, dalam minyak, 0,8 mm | 31 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 24 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 15 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 2.9 | - | IEC 60250 |
| Permittivitas relatif, 100 Hz | 3.1 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.8 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.001 | - | IEC 60250 |
| Faktor Dissipasi, 100 Hz | 0.002 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.01 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 175 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 100 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.71 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 3 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 30 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:07/27/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 245 - 260 | °C |
| Suhu Nozzle | 240 - 255 | °C |
| Suhu depan - Zona 3 | 245 - 260 | °C |
| Tengah - Zona 2 Suhu | 240 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 250 | °C |
| Suhu Cetakan | 50 - 75 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.013 - 0.025 | mm |
| Sumber GMD, terakhir diperbarui:07/27/2007 | ||
Produk jual panas (dalam persediaan)
PBT: 325,325FC,310,310SE0
PC+PBT: 357 357U,5220U,V3900WX
PBT +kaca yang diisi: DR51, DR48, 420 420se0, 553, 508, 420HP
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Valox Plastic 310SE0.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|