SabikXylex X8300MR resin adalah cetakan rilis versi X8300
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 47 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 46 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 150 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1520 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 71 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1680 | MPa | ASTM D 790 |
| Kekerasan, Pantai D, pembacaan 10S | 73 | - | ASTM D 2240 |
| Tekanan tarik, hasil, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 54 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | > 200 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 200 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1600 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 78 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1700 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 1121 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 95 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 96 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 79 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 75 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.04E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.23 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 60°C, aliran | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/120 | 96 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 80 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 265°C/2,16kg | 15 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.17 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 265°C/2,16 kg | 15 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 88 | % | ASTM D 1003 |
| Kabut | 1 | % | ASTM D 1003 |
| Indeks Refraksi | 1.539 | - | ISO 489 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | >1.E+15 | Ohm | ASTM D 257 |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 0 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| Glow Wire Flammability Index 750°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Sumber GMD, terakhir diperbarui:11/03/2004 | |||
Pengolahan
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 65 - 75 | °C |
| Waktu Pengeringan | 3 - 5 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 245 - 265 | °C |
| Suhu Nozzle | 245 - 265 | °C |
| Suhu depan - Zona 3 | 245 - 265 | °C |
| Tengah - Zona 2 Suhu | 240 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 250 | °C |
| Suhu Cetakan | 45 - 60 | °C |
| Tekanan Belakang | 0.2 - 0.5 | MPa |
| Kecepatan sekrup | 20 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.013 - 0.02 | mm |
| Sumber GMD, terakhir diperbarui:11/03/2004 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |