SabikXylex X8409AC resin adalah PC + Polyester, Injection (Blow) Molding, atau Extrusion Blow Molding kelas, Kemantapan Kimia dan Transparansi
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 57 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 6 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 92 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2370 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 94 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2220 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5.8 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 117 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2180 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 89 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 854 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 200 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 70 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -10°C | 8 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 8 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 123 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 116 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 104 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.04E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.23 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 60°C, aliran | 6.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 121 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 123 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 102 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 265°C/2,16kg | 4 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.2 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.37 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.13 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/2,16 kg | 3 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 88 | % | ASTM D 1003 |
| Kabut | 1.5 | % | ASTM D 1003 |
| Indeks Refraksi | 1.576 | - | ASTM D 542 |
| Sumber GMD, terakhir diperbarui:03/21/2006 | |||
Pengolahan
| Parameter | ||
| Pengeboran dengan Ekstrusi | Nilai | Satuan |
| Suhu Pengeringan | 75 - 90 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.01 - 0.02 | % |
| Suhu Peleburan (Parison) | 250 - 270 | °C |
| Barel - Zona 1 Suhu | 235 - 260 | °C |
| Barel - Zona 2 Suhu | 235 - 260 | °C |
| Barel - Zona 3 Suhu | 235 - 260 | °C |
| Barel - Zona 4 Suhu | 235 - 260 | °C |
| Adaptor - Zona 5 Suhu | 235 - 260 | °C |
| Kepala - Zona 6 - Suhu puncak | 240 - 270 | °C |
| Kepala - Zona 7 - Suhu rata-rata | 240 - 270 | °C |
| Kepala - Zona 7 - Suhu bawah | 240 - 270 | °C |
| Suhu Cetakan | 30 - 75 | °C |
| Sumber GMD, terakhir diperbarui:03/21/2006 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xylex X8409AC.pdf |
|