SabikXylex X7325WXresin adalahPC+Polyester, UV-stabil, tahan cuaca, tidak transparan
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 40 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 32 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4.7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 120 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1440 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 56 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1580 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 32 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4.2 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 119 | % | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 47 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1480 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 640 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 64 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 85 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 44 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 46 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 79 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 75 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 65 | °C | ASTM D 648 |
| Vicat Softening Temperature, Tingkat B/50 | 79 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 81 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 64 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.16 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 266°C/5,0 kgf | 42 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.15 | g/cm3 | ISO 1183 |
| Tingkat Aliran Peleburan, 250°C/5,0 kg | 19 | g/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 265°C/5,0 kg | 35 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:09/28/2004 | |||
Pengolahan
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 30 - 50 | °C |
| Waktu Pengeringan | 3 - 5 | jam |
| Waktu pengeringan (kumulatif) | 7 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 230 - 265 | °C |
| Suhu Nozzle | 230 - 265 | °C |
| Suhu depan - Zona 3 | 230 - 265 | °C |
| Tengah - Zona 2 Suhu | 240 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 250 | °C |
| Suhu Cetakan | 25 - 55 | °C |
| Tekanan Belakang | 0.2 - 0.5 | MPa |
| Kecepatan sekrup | 20 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.013 - 0.02 | mm |
| Sumber GMD, terakhir diperbarui:09/28/2004 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Xylex X7325WX.pdf |
|