SabikXylex FXY391DFresin adalahPC+Polyester paduan dalam Diffusion Visual fx. Kelas ini sesuai dengan peraturan kontak makanan FDA / Eropa AS. Paket warna dapat mempengaruhi kinerja.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 61 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 63 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 6 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 110 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2130 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 86 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2150 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 61 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 125 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2300 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 89 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2210 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 88 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 81 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 67 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 123 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 118 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 105 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.9E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 60°C, aliran | 7.1E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 122 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 124 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 113 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 265°C/2,16kg | 11 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.17 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.01 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.01 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/2,16 kg | 10 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:09/11/2008 | |||
Pengolahan
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 65 - 80 | °C |
| Waktu Pengeringan | 3 - 5 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 270 | °C |
| Suhu Nozzle | 250 - 270 | °C |
| Suhu depan - Zona 3 | 250 - 270 | °C |
| Tengah - Zona 2 Suhu | 245 - 270 | °C |
| Bagian belakang - Zona 1 Suhu | 245 - 260 | °C |
| Suhu Cetakan | 45 - 60 | °C |
| Tekanan Belakang | 0.1 - 0.5 | MPa |
| Kecepatan sekrup | 20 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.013 - 0.02 | mm |
| Sumber GMD, terakhir diperbarui:09/11/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xylex FXY391DF.pdf |
|