SabikXylex EXXX0005 resin adalahData awal: paduan PC + POLYESTER yang tidak diperkuat. aliran tinggi, tahan kimia dengan kualitas optik yang sangat baik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 48 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 51 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 150 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1760 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 83 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1880 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 150 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1900 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 71 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 854 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 94 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -10°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 106 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 90 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 85 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.19E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.23 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 60°C, aliran | 8.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/120 | 106 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 90 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 44 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 42 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 88 | % | ASTM D 1003 |
| Kabut | 2 | % | ASTM D 1003 |
| Sumber GMD, terakhir diperbarui:02/19/2002 |
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
Untuk informasi lebih lanjut silahkan unduh lembar data | |
| S-Plastics Xylex EXXX0005.pdf |