SabikVertonK3000Zresinadalah senyawa yang didasarkan pada resin Asetal yang mengandung Anti-Static.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 41 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 32 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 15.8 | % | ASTM D 638 |
| Tekanan tarik, putus | 59.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1590 | MPa | ASTM D 638 |
| Tekanan Flexural | 49 | MPa | ASTM D 790 |
| Modulus Flexural | 1440 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 41 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 36 | MPa | ISO 527 |
| Tekanan tarik, hasil | 13.3 | % | ISO 527 |
| Tekanan tarik, putus | 49.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1500 | MPa | ISO 527 |
| Tekanan Flexural | 40 | MPa | ISO 178 |
| Modulus Flexural | 1500 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | NB | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 28 | J | ASTM D 3763 |
| Dampak Multiaxial | 16 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 15 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 146 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 67 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.3E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.33E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 1.3E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.33E-04 | 1/°C | ISO 11359-2 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.32 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 2.29 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 1.8 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1.8 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 1.81 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 1.83 | % | ISO 294 |
| Pakai faktor pencuci | 14 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Dimodifikasi |
| COF Dinamis | 0.42 | - | ASTM D 3702 Dimodifikasi |
| COF statis | 0.25 | - | ASTM D 3702 Dimodifikasi |
| Kepadatan | 1.33 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 4.28 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+09 - 1.E+11 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 195 - 205 | °C |
| Suhu depan - Zona 3 | 200 - 210 | °C |
| Tengah - Zona 2 Suhu | 190 - 200 | °C |
| Bagian belakang - Zona 1 Suhu | 175 - 190 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Verton K3000Z.pdf |
|