SabikVertonPF007IX2resin adalahsenyawa yang didasarkan pada resin PA 6 yang mengandung Serat Kaca.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 125 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 123 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2.9 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 8700 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 171 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 4 | % | ISO 178 |
| Flexural Modulus, 2 mm/menit | 6800 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 55 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 20 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 60°C, aliran | 2.7E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 1.22E-04 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 217 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran | 0.2 | % | Metode S-Plastics |
| Kepadatan | 1.36 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:11/16/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 265 - 275 | °C |
| Suhu depan - Zona 3 | 275 - 290 | °C |
| Tengah - Zona 2 Suhu | 265 - 275 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 260 | °C |
| Suhu Cetakan | 80 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:11/16/2007 | ||