SabikVertonM3000resinadalah senyawa yang didasarkan pada resin polipropilena yang mengandung Anti-Static.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 28 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 18 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 9.6 | % | ASTM D 638 |
| Tekanan tarik, putus | 47 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1390 | MPa | ASTM D 638 |
| Tekanan Flexural | 40 | MPa | ASTM D 790 |
| Modulus Flexural | 1440 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 28 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 7 | MPa | ISO 527 |
| Tekanan tarik, hasil | 8 | % | ISO 527 |
| Tekanan tarik, putus | 98.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1350 | MPa | ISO 527 |
| Tekanan Flexural | 32 | MPa | ISO 178 |
| Modulus Flexural | 1360 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 69 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 7 | J | ASTM D 3763 |
| Dampak Multiaxial | 5 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 100 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 56 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.1E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.28E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 1.1E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.28E-04 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 103 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 59 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 0.95 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.85 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 1.4 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1.3 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 1.35 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 1.33 | % | ISO 294 |
| Kepadatan | 0.95 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+09 - 1.E+11 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 70 - 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 190 - 200 | °C |
| Suhu depan - Zona 3 | 200 - 210 | °C |
| Tengah - Zona 2 Suhu | 195 - 205 | °C |
| Bagian belakang - Zona 1 Suhu | 180 - 195 | °C |
| Suhu Cetakan | 30 - 50 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |