SabikVerton63000CTCresin adalahSebuah senyawa PC-Alloy antistatik permanen yang memiliki transparansi dan kebersihan yang unggul untuk aplikasi kemasan semikonduktor canggih
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 35 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 0 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 10 mm/menit | 0 | % | Metode S-Plastics - Jepang |
| Tekanan tarik, brk, tipe I, 10 mm/menit | 200 | % | Metode S-Plastics - Jepang |
| Tensile Modulus, 50 mm/min | 1170 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 52 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1170 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 34 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 0 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 0 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 140 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1190 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/menit | 1150 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 0 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 580 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 0 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 0 | kJ/m2 | ISO 180/1A |
| Charpy Impact, bertanduk, 23°C | 69 | kJ/m2 | ISO 179/2C |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 84 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 75 | °C | ASTM D 648 |
| CTE, 23°C sampai 60°C, aliran | 1.2E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 1.4E-04 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 0 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.16 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0 | % | ASTM D 570 |
| Penyusutan jamur, aliran | 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, aliran | 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 24 jam | 0 - 0 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0 - 0 | % | ASTM D 955 |
| Kepadatan | 0 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.7 | % | ISO 62 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 77 | % | ASTM D 1003 |
| Kabut | 25 | % | ASTM D 1003 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 8.E+09 - 3.E+11 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 9.E+09 - 4.E+11 | Ohm | ASTM D 257 |
| Kerusakan statis, 5000V hingga <50V | 2 | < detik | FTMS101B |
| Resistensi permukaan, ROA | 0.E+00 - 0.E+00 | Ohm | IEC 60093 |
| Sumber GMD, terakhir diperbarui:08/21/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 - 95 | °C |
| Waktu Pengeringan | 6 - 8 | jam |
| Suhu Peleburan | 230 - 250 | °C |
| Suhu Nozzle | 230 - 250 | °C |
| Suhu depan - Zona 3 | 230 - 250 | °C |
| Tengah - Zona 2 Suhu | 225 - 240 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 230 | °C |
| Suhu Cetakan | 40 - 50 | °C |
| Sumber GMD, terakhir diperbarui:08/21/2007 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Verton 63000CTC.pdf |
|