SabikVerton9X03508resinadalah senyawa berbasis resin PPO+PA66 yang mengandung Flame Retardant, Anti-Static.
Bahan termasuk: Antistat, Flame Retardant, High Impact.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 53 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 53 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 2.1 | % | ASTM D 638 |
| Tekanan tarik, putus | 2.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 4820 | MPa | ASTM D 638 |
| Tekanan Flexural | 82 | MPa | ASTM D 790 |
| Modulus Flexural | 3440 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 59 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 58 | MPa | ISO 527 |
| Tekanan tarik, hasil | 2.4 | % | ISO 527 |
| Tekanan tarik, putus | 2.8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 4470 | MPa | ISO 527 |
| Tekanan Flexural | 96 | MPa | ISO 178 |
| Modulus Flexural | 4000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 427 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 37 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 8 | J | ASTM D 3763 |
| Dampak Multiaxial | 1 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 26 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 230 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 186 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.48E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 4.32E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 6.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 4.3E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 218 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 179 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.31 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.9 | % | ASTM D 570 |
| Kepadatan | 1.31 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+03 - 1.E+05 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 200 - 230 | °C |
| Suhu depan - Zona 3 | 220 - 230 | °C |
| Tengah - Zona 2 Suhu | 210 - 220 | °C |
| Bagian belakang - Zona 1 Suhu | 200 - 210 | °C |
| Suhu Cetakan | 40 - 55 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Verton 9X03508.pdf |
|