SabikVertonRX09010resinadalah senyawa berbasis resin Nylon 66 yang mengandung Serat Kaca, Filler Termal Proprietary.
bahan ini termasuk; Konduktif termal, Non-Brominated & Non-Chlorinated Flame Retardant, Mudah Molding.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 94 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.4 | % | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 139 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 9500 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 20 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 2 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Konduktivitas Termal | 1 | W/m-°C | ASTM E 1530 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 192 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran (5) | 0.2 - 0.4 | % | Metode S-Plastics |
| Kepadatan | 1.72 | g/cm3 | ISO 1183 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 1.6 | mm | UL 94 oleh GE |
| Glow Wire Flammability Index 960°C, melewati pada | 1.6 | mm | IEC 60695-2-12 |
| Sumber GMD, terakhir diperbarui:2009/07/02 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 265 - 275 | °C |
| Suhu depan - Zona 3 | 260 - 270 | °C |
| Tengah - Zona 2 Suhu | 255 - 265 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 260 | °C |
| Suhu Cetakan | 60 - 100 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:2009/07/02 | ||
Produk terkait lainnya yang kami rekomendasikan:
Untuk informasi lebih lanjut silahkan download lembar data | |
 | S-Plastics Verton RX09010.pdf |