SabikVertonITF2Bresinadalah senyawa berbasis resin Nylon 6/12 yang mengandung Serat Kaca, Filler Termal Proprietary.
Bahan termasuk: Termal Konduktif.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 79 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 2.1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 9980 | MPa | ASTM D 638 |
| Tekanan Flexural | 144 | MPa | ASTM D 790 |
| Modulus Flexural | 9250 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 80 | MPa | ISO 527 |
| Tekanan tarik, putus | 2.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 10200 | MPa | ISO 527 |
| Tekanan Flexural | 144 | MPa | ISO 178 |
| Modulus Flexural | 9500 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 421 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 32 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 8 | J | ASTM D 3763 |
| Dampak Multiaxial | 1 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 28 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 167 | °C | ASTM D 648 |
| Konduktivitas Termal | 1.1 | W/m-°C | ASTM E 1530 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 158 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran, 24 jam | 0.9 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1.5 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.89 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 1.45 | % | ISO 294 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.12 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.12 - 0.2 | % |
| Suhu Peleburan | 270 - 275 | °C |
| Suhu depan - Zona 3 | 270 - 280 | °C |
| Tengah - Zona 2 Suhu | 260 - 270 | °C |
| Bagian belakang - Zona 1 Suhu | 255 - 265 | °C |
| Suhu Cetakan | 65 - 95 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Verton ITF2B.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|