SabikFaradexDX07304resin adalahKelas CF yang diisi dengan pelindung EMI
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 133 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 23190 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 210 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 207 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 19600 | MPa | ASTM D 790 |
| Modulus tarik, 1 mm/menit | 23380 | MPa | ISO 527 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 296 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 37 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 15 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 72 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 72 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.4 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.17 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.21 | % | ASTM D 955 |
| Kepadatan | 1.4 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 300°C/2,16 kg | 11 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 7.3E+03 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 4.38E+05 | Ohm | ASTM D 257 |
| Resistivitas Volume | 5.E+04 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | 1.E+04 | Ohm | IEC 60093 |
| Efektivitas Perisai @ 3mm | 30 | dB | Metode S-Plastics |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:06/20/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 85 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 270 - 300 | °C |
| Suhu Nozzle | 265 - 300 | °C |
| Suhu depan - Zona 3 | 265 - 300 | °C |
| Tengah - Zona 2 Suhu | 260 - 300 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 300 | °C |
| Suhu Cetakan | 60 - 90 | °C |
| Tekanan Belakang | 4 | MPa |
| Kecepatan sekrup | 30 - 100 | rpm |
| Sumber GMD, terakhir diperbarui:06/20/2007 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Faradex DX07304.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|