SabikColorcompW10009Iresin adalahsenyawa yang didasarkan pada resin polibutilen terefalat yang mengandung Flame Retardant.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 42 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 4.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1900 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 68 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1900 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 125 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 201 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 60 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran | 2.3 | % | Metode S-Plastics |
| Kepadatan | 1.39 | g/cm3 | ISO 1183 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 1.6 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:01/14/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 245 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 260 | °C |
| Tengah - Zona 2 Suhu | 245 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C |
| Suhu Cetakan | 80 - 100 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:01/14/2008 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Colorcomp W10009I.pdf |
|