SabikColorcompM1000Sresin adalahsebuah senyawa berbasis resin polipropilena yang mengandung Unfilled Glow In the Dark Custom Color.
Fitur material ini meliputi: Stabilisasi panas.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 28 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 26 | MPa | ISO 527 |
| Tekanan tarik, hasil | 7 | % | ISO 527 |
| Tekanan tarik, putus | 40 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2160 | MPa | ISO 527 |
| Tekanan Fleksural | 40 | MPa | ISO 178 |
| Modulus Flexural | 1800 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 3 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 130 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 94 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.13 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 1.5 - 1.7 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1.5 - 1.7 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 1.51 - 1.67 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 1.51 - 1.67 | % | ISO 294 |
| Kepadatan | 1.12 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:09/28/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 215 - 220 | °C |
| Suhu depan - Zona 3 | 205 - 215 | °C |
| Tengah - Zona 2 Suhu | 200 - 210 | °C |
| Bagian belakang - Zona 1 Suhu | 195 - 205 | °C |
| Suhu Cetakan | 30 - 50 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/28/2004 | ||
|