SabikColorcompJX91550resin adalahsebuah senyawa berbasis resin Polyethersulfone yang mengandung Unfilled Custom Color.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 77 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 58 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 5.6 | % | ASTM D 638 |
| Tekanan tarik, putus | 13.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2930 | MPa | ASTM D 638 |
| Tekanan Fleksural | 122 | MPa | ASTM D 790 |
| Modulus Flexural | 2890 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 78 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 53 | MPa | ISO 527 |
| Tekanan tarik, hasil | 6.2 | % | ISO 527 |
| Tekanan tarik, putus | 23.4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2830 | MPa | ISO 527 |
| Tekanan Fleksural | 118 | MPa | ISO 178 |
| Modulus Flexural | 2920 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 19 | J | ASTM D 3763 |
| Dampak Multiaxial | 32 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 176 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 5.05E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.14E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 5.07E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 5.15E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 187 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.49 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.6 - 0.8 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.7 - 0.9 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.6 - 0.8 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.7 - 0.9 | % | ISO 294 |
| Kepadatan | 1.49 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.76 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:10/05/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 355 - 370 | °C |
| Suhu depan - Zona 3 | 370 - 380 | °C |
| Tengah - Zona 2 Suhu | 360 - 370 | °C |
| Bagian belakang - Zona 1 Suhu | 345 - 355 | °C |
| Suhu Cetakan | 140 - 150 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 60 - 100 | rpm |
| Sumber GMD, terakhir diperbarui:10/05/2004 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Colorcomp JX91550.pdf |
|