SabikColorcompJ1000Zresin adalahsenyawa yang didasarkan pada resin Polyethersulfone.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 50 mm/menit | 89 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 72 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2600 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 130 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2800 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 206 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran | 1 | % | Metode S-Plastics |
| Kepadatan | 1.37 | g/cm3 | ISO 1183 |
| Penyerapan air, 23°C/24 jam | 1.8 | % | ISO 62-1 |
| Sumber GMD, terakhir diperbarui:03/03/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 355 - 370 | °C |
| Suhu depan - Zona 3 | 370 - 380 | °C |
| Tengah - Zona 2 Suhu | 360 - 370 | °C |
| Bagian belakang - Zona 1 Suhu | 345 - 355 | °C |
| Suhu Cetakan | 140 - 150 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 60 - 100 | rpm |
| Sumber GMD, terakhir diperbarui:03/03/2008 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Colorcomp J1000Z.pdf |
|