SabikCycolacXMG94Uresin adalahTingkat cetakan ABS yang stabilisasi UV dengan aliran tinggi
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 46 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 35 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 18 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2480 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 79 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2620 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 35 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 35 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2450 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 65 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2500 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 240 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 80 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 21 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 18 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 7 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 23 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 98 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 95 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 82 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.82E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 8.46E-05 | 1/°C | ASTM E 831 |
| Vicat Softening Temperature, Tingkat B/50 | 99 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 100 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 82 | °C | ISO 75/Af |
| Indeks suhu relatif, Elec | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 60 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.04 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 230°C/3,8 kgf | 11.7 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.06 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.16 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 12 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:07/25/2005 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.01 | % |
| Suhu Peleburan | 205 - 245 | °C |
| Suhu Nozzle | 205 - 245 | °C |
| Suhu depan - Zona 3 | 205 - 225 | °C |
| Tengah - Zona 2 Suhu | 200 - 210 | °C |
| Bagian belakang - Zona 1 Suhu | 190 - 200 | °C |
| Suhu Cetakan | 50 - 70 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Menembak untuk ukuran silinder | 50 - 70 | % |
| Kedalaman ventilasi | 0.038 - 0.051 | mm |
| Sumber GMD, terakhir diperbarui:07/25/2005 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|