SabikCycolacX37resin adalahABS, cetakan injeksi, tingkat panas tinggi.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 48 | MPa | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2410 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 82 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2410 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 109 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 213 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -40°C | 53 | J/m | ASTM D 256 |
| Gardner, 23°C | 13 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 103 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.92E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 60 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.05 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 230°C/3,8 kgf | 1 | g/10 menit | ASTM D 1238 |
| Optik | Nilai | Satuan | Standar |
| Berkilau, tidak bertekstur, 60 derajat | 94 | - | ASTM D 523 |
| Listrik | Nilai | Satuan | Standar |
| Kekuatan dielektrik, di udara, 1,6 mm | 36.8 | kV/mm | ASTM D 149 |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 3 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 1 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 0 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.6 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:12/29/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 95 - 100 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.01 | % |
| Suhu Peleburan | 245 - 275 | °C |
| Suhu Nozzle | 245 - 275 | °C |
| Suhu depan - Zona 3 | 245 - 255 | °C |
| Tengah - Zona 2 Suhu | 225 - 240 | °C |
| Bagian belakang - Zona 1 Suhu | 200 - 210 | °C |
| Suhu Cetakan | 50 - 80 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Menembak untuk ukuran silinder | 50 - 70 | % |
| Kedalaman ventilasi | 0.038 - 0.051 | mm |
| Sumber GMD, terakhir diperbarui:12/29/1999 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Cycolac X37.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|