SabikStat-konRX04031resin adalahsenyawa berbasis resin PA66 yang mengandung Serat Karbon, Serat Kaca, Retardant Api
termasuk: Non-Brominated & Non-Chlorinated Flame Retardant, Electrically Conductive, Mudah Molding.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, pecah, 5 mm/menit | 184 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 264 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 15000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 63 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 218 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran | 0.2 | % | Metode S-Plastics |
| Kepadatan | 1.47 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+03 - 1.E+04 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.8 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 1.6 | mm | IEC 60695-2-12 |
| Sumber GMD, terakhir diperbarui:04/07/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 265 - 275 | °C |
| Suhu depan - Zona 3 | 260 - 270 | °C |
| Tengah - Zona 2 Suhu | 255 - 265 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 260 | °C |
| Suhu Cetakan | 60 - 100 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:04/07/2008 | ||