SabikStat-konRE0039resin adalahsenyawa yang didasarkan pada resin Nylon 66 yang mengandung Serat Karbon, Flame Retardant.
Bahan termasuk: Konduktif listrik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 205 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 2.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 17580 | MPa | ASTM D 638 |
| Tekanan Flexural | 297 | MPa | ASTM D 790 |
| Modulus Flexural | 11440 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 209 | MPa | ISO 527 |
| Tekanan tarik, putus | 2.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 15600 | MPa | ISO 527 |
| Tekanan Flexural | 318 | MPa | ISO 178 |
| Modulus Flexural | 14200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 704 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 74 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 8 | J | ASTM D 3763 |
| Dampak Multiaxial | 2 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 46 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 247 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 4.57E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 4.57E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.61E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 228 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.44 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.55 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.2 - 0.3 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.7 - 0.8 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.17 - 0.26 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.68 - 0.78 | % | ISO 294 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.87 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 1.5 | mm | UL 94 oleh GE |
| Sesuai UL, 94-5VA rating (3)(4) | 1.5 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 280 - 305 | °C |
| Suhu depan - Zona 3 | 295 - 305 | °C |
| Tengah - Zona 2 Suhu | 280 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 265 - 275 | °C |
| Suhu Cetakan | 95 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon RE0039.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|