SabikStat-konRE004resin adalahsenyawa berbasis resin Nylon 66 yang mengandung Serat Karbon. Fitur tambahan dari bahan ini meliputi:
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 219 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 4.3 | % | ASTM D 638 |
| Tekanan Flexural | 312 | MPa | ASTM D 790 |
| Modulus Flexural | 12340 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 233 | MPa | ISO 527 |
| Tekanan tarik, putus | 2.9 | % | ISO 527 |
| Tekanan Flexural | 337 | MPa | ISO 178 |
| Modulus Flexural | 14600 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 523 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 64 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 54 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.25 | g/cm3 | ASTM D 792 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94HB (3) | 1.5 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 280 - 305 | °C |
| Suhu depan - Zona 3 | 295 - 305 | °C |
| Tengah - Zona 2 Suhu | 280 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 265 - 275 | °C |
| Suhu Cetakan | 95 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||