SabikStat-konPX08019resin adalahsenyawa berbasis resin PA 6 yang mengandung Serat Kaca, Serat Karbon, Retardant Api.
termasuk; Non-Halogen Flame Retardant, Electrically Conductive.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 160 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.3 | % | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 230 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 11500 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 45 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 207 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran | 0.2 - 0.4 | % | Metode S-Plastics |
| Kepadatan | 1.31 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+04 - 1.E+06 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 1.6 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:12/17/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 75 - 85 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Suhu Peleburan | 250 - 270 | °C |
| Suhu depan - Zona 3 | 250 - 270 | °C |
| Tengah - Zona 2 Suhu | 250 - 270 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 260 | °C |
| Suhu Cetakan | 70 - 90 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:12/17/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon PX08019.pdf |
|