SabikStat-konPE002resin adalahsenyawa berbasis resin Nylon 6 yang mengandung Serat Karbon. Fitur tambahan dari bahan ini meliputi:
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 114 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 115 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 6.8 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 6.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 11720 | MPa | ASTM D 638 |
| Tekanan Flexural | 172 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 179 | MPa | ASTM D 790 |
| Modulus Flexural | 5510 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 5520 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 124 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 124 | MPa | ISO 527 |
| Tekanan tarik, putus | 8 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 8.1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 8670 | MPa | ISO 527 |
| Tekanan Flexural | 185 | MPa | ISO 178 |
| Tekanan lentur, hasil, 2 mm/menit | 185 | MPa | ISO 178 |
| Modulus Flexural | 7400 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 7400 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 122 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 64 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 219 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 197 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.1E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 3.96E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 3.9E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, aliran | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 3.9E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 197 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.18 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 1 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.3 - 0.5 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.6 - 0.8 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.41 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.74 | % | ISO 294 |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 265 - 275 | °C |
| Suhu depan - Zona 3 | 275 - 290 | °C |
| Tengah - Zona 2 Suhu | 265 - 275 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 260 | °C |
| Suhu Cetakan | 80 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon PE002.pdf |
|