SabikStat-konOEL13Iresin adalahresin dasar linear-PPS yang mengandung Serat Karbon dan PTFE Lubricant. Karakteristik kelas ini adalah High Impact.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 132 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 13950 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 195 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 10510 | MPa | ASTM D 790 |
| Tekanan tarik, pecah, 5 mm/menit | 130 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 16590 | MPa | ISO 527 |
| Tekanan Flexural | 218 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 11920 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 601 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 93 | J/m | ASTM D 256 |
| Dampak Multiaxial | 3 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 16 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 35 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 273 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 213 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 1.4E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 6.E-05 | 1/°C | ASTM D 696 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 260 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 212 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.37 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.2 - 0.4 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.7 - 0.9 | % | ASTM D 955 |
| Kepadatan | 1.37 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+00 - 3.E+00 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 2.E+00 - 4.E+00 | Ohm | ASTM D 257 |
| Resistensi permukaan, ROA | 1.E+00 - 3.E+00 | Ohm | IEC 60093 |
| Sumber GMD, terakhir diperbarui:11/25/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 315 - 320 | °C |
| Suhu depan - Zona 3 | 330 - 345 | °C |
| Tengah - Zona 2 Suhu | 320 - 330 | °C |
| Bagian belakang - Zona 1 Suhu | 305 - 315 | °C |
| Suhu Cetakan | 140 - 165 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:11/25/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon OEL13I.pdf |
|