SabikStat-konOE006Aresin adalahsenyawa yang didasarkan pada PPS - resin bercabang yang mengandung Serat Karbon.
termasuk: Konduktif listrik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 210 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 32750 | MPa | ASTM D 638 |
| Tekanan Flexural | 304 | MPa | ASTM D 790 |
| Modulus Flexural | 23510 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 204 | MPa | ISO 527 |
| Tekanan tarik, putus | 1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 25450 | MPa | ISO 527 |
| Tekanan Flexural | 311 | MPa | ISO 178 |
| Modulus Flexural | 24720 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 437 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 49 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 3 | J | ASTM D 3763 |
| Dampak Multiaxial | 1 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 28 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 266 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.2E-06 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 3.96E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 8.7E-06 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 4.08E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 268 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.44 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.02 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.1 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.4 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.08 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.4 | % | ISO 294 |
| Pakai faktor pencuci | 857 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Dimodifikasi |
| COF Dinamis | 1.6 | - | ASTM D 3702 Dimodifikasi |
| COF statis | 1.38 | - | ASTM D 3702 Dimodifikasi |
| Kepadatan | 1.44 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.03 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 1 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 315 - 320 | °C |
| Suhu depan - Zona 3 | 330 - 345 | °C |
| Tengah - Zona 2 Suhu | 320 - 330 | °C |
| Bagian belakang - Zona 1 Suhu | 305 - 315 | °C |
| Suhu Cetakan | 140 - 165 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon OE006A.pdf |
|