SabikStat-konOE006resin adalahsenyawa yang didasarkan pada PPS - resin linier yang mengandung Serat Karbon.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 186 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 23920 | MPa | ASTM D 638 |
| Tekanan Flexural | 282 | MPa | ASTM D 790 |
| Modulus Flexural | 21160 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 640 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 74 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 108 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.43 | g/cm3 | ASTM D 792 |
| Sumber GMD, terakhir diperbarui:2010/03/16 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 315 - 320 | °C |
| Suhu depan - Zona 3 | 330 - 345 | °C |
| Tengah - Zona 2 Suhu | 320 - 330 | °C |
| Bagian belakang - Zona 1 Suhu | 305 - 315 | °C |
| Suhu Cetakan | 140 - 165 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:2010/03/16 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon OE006.pdf |
|