SabikStat-konOE004AEresin adalahsenyawa yang didasarkan pada resin PPS (bercabang) yang mengandung serat karbon.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 163 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 163 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0.8 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 0.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 27160 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 215 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 15710 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 146 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 146 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 0.8 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 0.8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 19120 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 208 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 16050 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 254 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 47 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 12 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 279 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 263 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 262 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.42 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.1 - 0.3 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.5 - 0.7 | % | ASTM D 955 |
| Kepadatan | 1.42 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 2.E+00 - 4.E+00 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:03/26/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 315 - 320 | °C |
| Suhu depan - Zona 3 | 330 - 345 | °C |
| Tengah - Zona 2 Suhu | 320 - 330 | °C |
| Bagian belakang - Zona 1 Suhu | 305 - 315 | °C |
| Suhu Cetakan | 140 - 165 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/26/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon OE004AE.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|