SabikStat-konMFD03resin adalahsenyawa yang didasarkan pada resin polipropilena yang mengandung Serat Kaca, Serbuk Karbon.
Bahan termasuk: Konduktif listrik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 34 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 16 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 2.7 | % | ASTM D 638 |
| Tekanan tarik, putus | 6.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 3440 | MPa | ASTM D 638 |
| Modulus Flexural | 2750 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 34 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 15 | MPa | ISO 527 |
| Tekanan tarik, hasil | 2.6 | % | ISO 527 |
| Tekanan tarik, putus | 5.7 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3310 | MPa | ISO 527 |
| Tekanan Flexural | 51 | MPa | ISO 178 |
| Modulus Flexural | 3000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 138 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 347 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 13 | J | ASTM D 3763 |
| Dampak Multiaxial | 5 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 12 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 22 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 147 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 106 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.04E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 4.68E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 1.05E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 4.7E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.07 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 1 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.9 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 1 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.92 | % | ISO 294 |
| Kepadatan | 1.07 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:09/26/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 225 - 250 | °C |
| Suhu depan - Zona 3 | 240 - 250 | °C |
| Tengah - Zona 2 Suhu | 215 - 225 | °C |
| Bagian belakang - Zona 1 Suhu | 195 - 205 | °C |
| Suhu Cetakan | 30 - 50 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/26/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon MFD03.pdf |
|