SabikStat-konME003Sresin adalahsenyawa yang didasarkan pada resin polipropilena yang mengandung Serat Karbon. Fitur tambahan dari bahan ini meliputi:
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 47 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 39 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 0.7 | % | ASTM D 638 |
| Tekanan tarik, putus | 1.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 8960 | MPa | ASTM D 638 |
| Tekanan Flexural | 65 | MPa | ASTM D 790 |
| Modulus Flexural | 6890 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 47 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 44 | MPa | ISO 527 |
| Tekanan tarik, hasil | 0.7 | % | ISO 527 |
| Tekanan tarik, putus | 1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 8590 | MPa | ISO 527 |
| Tekanan Flexural | 62 | MPa | ISO 178 |
| Modulus Flexural | 7000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 128 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 16 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 14 | J | ASTM D 3763 |
| Dampak Multiaxial | 3 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 1 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 153 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 133 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.02E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 2.88E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 2.9E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 150 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 131 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 0.99 | g/cm3 | ASTM D 792 |
| Sumber GMD, terakhir diperbarui:08/02/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 225 - 250 | °C |
| Suhu depan - Zona 3 | 240 - 250 | °C |
| Tengah - Zona 2 Suhu | 215 - 225 | °C |
| Bagian belakang - Zona 1 Suhu | 195 - 205 | °C |
| Suhu Cetakan | 30 - 50 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:08/02/2007 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon ME003S.pdf |
|