SabikStat-konKX02764resin adalahsenyawa yang didasarkan pada resin Asetal yang mengandung Carbon Powder.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 53 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 47 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 3.8 | % | ASTM D 638 |
| Tekanan tarik, putus | 10.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 3480 | MPa | ASTM D 638 |
| Tekanan Flexural | 100 | MPa | ASTM D 790 |
| Modulus Flexural | 3010 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 53 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 46 | MPa | ISO 527 |
| Tekanan tarik, hasil | 4 | % | ISO 527 |
| Tekanan tarik, putus | 18.1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3460 | MPa | ISO 527 |
| Tekanan Flexural | 96 | MPa | ISO 178 |
| Modulus Flexural | 3010 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 373 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 42 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 3 | J | ASTM D 3763 |
| Dampak Multiaxial | 7 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 52 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 106 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 103 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.443 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.18 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 1.5 - 3.5 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 1.5 - 3.5 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 1.5 - 3.5 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 1.5 - 3.5 | % | ISO 294 |
| Kepadatan | 1.43 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.25 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+02 - 1.E+06 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 200 - 215 | °C |
| Suhu depan - Zona 3 | 210 - 220 | °C |
| Tengah - Zona 2 Suhu | 195 - 205 | °C |
| Bagian belakang - Zona 1 Suhu | 175 - 190 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon KX02764.pdf |
|