SabikStat-konKEP33resin adalahsenyawa yang didasarkan pada resin Asetal yang mengandung Serat Karbon, Silikon, PTFE. Fitur tambahan dari bahan ini
termasuk: Konduktif listrik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 77 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 10200 | MPa | ASTM D 638 |
| Tekanan Flexural | 114 | MPa | ASTM D 790 |
| Modulus Flexural | 7140 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 74 | MPa | ISO 527 |
| Tekanan tarik, putus | 1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 10170 | MPa | ISO 527 |
| Tekanan Flexural | 106 | MPa | ISO 178 |
| Modulus Flexural | 8270 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 128 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 32 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 7 | J | ASTM D 3763 |
| Dampak Multiaxial | 4 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 17 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 3 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 66 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 155 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.473 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.21 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.4 - 0.6 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.7 - 0.9 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.4 - 0.6 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.7 - 0.9 | % | ISO 294 |
| Pakai faktor pencuci | 202 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Dimodifikasi |
| COF Dinamis | 0.36 | - | ASTM D 3702 Dimodifikasi |
| COF statis | 0.31 | - | ASTM D 3702 Dimodifikasi |
| Kepadatan | 1.46 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.32 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+01 - 1.E+04 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+01 - 1.E+04 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 200 - 215 | °C |
| Suhu depan - Zona 3 | 210 - 220 | °C |
| Tengah - Zona 2 Suhu | 195 - 205 | °C |
| Bagian belakang - Zona 1 Suhu | 175 - 190 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |