SabikStat-konIS000LXresin adalahsebuah senyawa yang didasarkan pada Nylon 6/12 yang mengandung Serat Baja Rinsing.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 67 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 9.3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 10.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 3040 | MPa | ASTM D 638 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2670 | MPa | ASTM D 790 |
| Tekanan tarik, pecah, 5 mm/menit | 66 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 8.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3070 | MPa | ISO 527 |
| Tekanan Flexural | 82 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2430 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 486 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 27 | J/m | ASTM D 256 |
| Dampak Multiaxial | 0 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 2 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 35 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 3 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 180 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 92 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 1.02E-04 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 1.19E-04 | 1/°C | ASTM D 696 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 161 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 72 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.18 | - | ASTM D 792 |
| Kepadatan | 1.18 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.2 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam (5) | 1 - 3 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam (5) | 2 - 4 | % | ASTM D 955 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.29 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:2010/04/05 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.12 - 0.2 | % |
| Suhu Peleburan | 270 - 275 | °C |
| Suhu depan - Zona 3 | 270 - 280 | °C |
| Tengah - Zona 2 Suhu | 260 - 270 | °C |
| Bagian belakang - Zona 1 Suhu | 255 - 265 | °C |
| Suhu Cetakan | 65 - 95 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:2010/04/05 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |