SabikStat-konEXCP0023resin adalahData awal: 40% PPS diperkuat serat karbon. Konduktif: Peralatan otomotif dan bisnis.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 188 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 188 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0.8 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 0.7 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/menit | 30890 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 249 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 23710 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 395 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 37 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 4 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 267 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.46 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 4.E+00 | Ohm-cm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:09/27/2001 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 140 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 305 - 330 | °C |
| Suhu Nozzle | 305 - 320 | °C |
| Suhu depan - Zona 3 | 315 - 330 | °C |
| Tengah - Zona 2 Suhu | 305 - 315 | °C |
| Bagian belakang - Zona 1 Suhu | 290 - 305 | °C |
| Suhu Cetakan | 140 - 160 | °C |
| Tekanan Belakang | 0.3 | MPa |
| Sumber GMD, terakhir diperbarui:09/27/2001 | ||