SabikStat-konEE006resin adalahsenyawa yang didasarkan pada resin Polyetherimide yang mengandung Serat Karbon. Fitur tambahan dari bahan ini meliputi:
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 196 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 19440 | MPa | ASTM D 638 |
| Tekanan Flexural | 280 | MPa | ASTM D 790 |
| Modulus Flexural | 18170 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 183 | MPa | ISO 527 |
| Tekanan tarik, putus | 1.1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 20870 | MPa | ISO 527 |
| Tekanan Flexural | 269 | MPa | ISO 178 |
| Modulus Flexural | 17930 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 373 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 42 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 8 | J | ASTM D 3763 |
| Dampak Multiaxial | 2 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 26 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 217 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 3.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 2.16E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 3.64E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 2.25E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 219 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.39 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.2 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.1 - 0.3 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.3 - 0.5 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.1 - 0.3 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.3 - 0.5 | % | ISO 294 |
| Pakai faktor pencuci | 75 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Dimodifikasi |
| COF Dinamis | 0.52 | - | ASTM D 3702 Dimodifikasi |
| COF statis | 0.48 | - | ASTM D 3702 Dimodifikasi |
| Kepadatan | 1.39 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.29 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 360 - 365 | °C |
| Suhu depan - Zona 3 | 365 - 375 | °C |
| Tengah - Zona 2 Suhu | 355 - 365 | °C |
| Bagian belakang - Zona 1 Suhu | 345 - 355 | °C |
| Suhu Cetakan | 120 - 150 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 60 - 100 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon EE006.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|