SabikStat-konPDXD05301CCS resin adalahSenyawa Polikarbonat yang aman dengan Low Ionic, Low Outgassing, Low LPC dan ESD cocok untuk Semikonduktor dan Hard Disk Drive (HDD)
aplikasi
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 48 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 60 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 5.3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 9.9 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/menit | 2590 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 95 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2280 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 56 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 56 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1.5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2490 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 77 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2480 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 54 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 51 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 6 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 149 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 132 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 5.1E-01 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.2E-01 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 5.1E-01 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 5.2E-01 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 148 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 146 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 131 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.22 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.6 - 0.74 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/5,0 kgf | 22.6 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.22 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.8 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.34 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/5,0 kg | 22 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:10/22/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 305 - 325 | °C |
| Suhu depan - Zona 3 | 320 - 330 | °C |
| Tengah - Zona 2 Suhu | 310 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 295 - 305 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/22/2007 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon PDXD05301CCS.pdf |
|