SabikStat-kon Noryl_HMC3008A resinadalah 30% resin diperkuat serat kaca/mineral/karbon; dissipative statis; 250F (120C) HDT.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 99 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 104 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 4 | % | ASTM D 638 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 127 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 9850 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 120 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 77 | mg/1000cy | ASTM D 1044 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 149 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 121 | °C | ASTM D 648 |
| Indeks suhu relatif, Elec | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 50 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.28 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.06 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.05 - 0.15 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.15 - 0.3 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+03 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+05 | Ohm | ASTM D 257 |
| Kerusakan statis, 5000V hingga <50V | 0.01 | < detik | FTMS101B |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL Diakui, Kelas Api 94V-1 (3) | 2.48 | mm | UL 94 |
| Indeks Oksigen (LOI) | 39 | % | ASTM D 2863 |
| Sumber GMD, terakhir diperbarui:03/15/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 100 - 105 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 270 - 300 | °C |
| Suhu Nozzle | 270 - 300 | °C |
| Suhu depan - Zona 3 | 260 - 300 | °C |
| Tengah - Zona 2 Suhu | 250 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 290 | °C |
| Suhu Cetakan | 65 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 20 - 100 | rpm |
| Menembak untuk ukuran silinder | 30 - 70 | % |
| Kedalaman ventilasi | 0.038 - 0.051 | mm |
| Sumber GMD, terakhir diperbarui:03/15/1999 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon Noryl_HMC3008A.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|